Supervisor: Prof. Bert Klumperman2024-12-122024-12-12https://dspace.academy.edu.ly/handle/123456789/875The synthesis of polymerizable RhB-based nanocolorants is described. Poly(AAm-co-RhB) nanocolorants were successfully synthesized for the first time via inverse miniemulsion polymerization. RhB dye was first functionalized by esterification reaction to introduce an acrylate polymerizable group. The RhB-acrylate dye was copolymerized with AAm monomer in an inverse miniemulsion polymerization to produce nanocolorants with superior light and migration fastness. Crosslinked-poly(AAm-co-RhB) nanocolorants could be obtained based on the incorporation of a crosslinking agent. Poly(AAm-co-RhB) and crosslinked-poly(AAm co-RhB) nanocolorants exhibited a morphology of dark solid and core-shell particles, respectively. In both nanocolorants, the RhB-acrylate dye was completely integrated by copolymerization into the polymer matrix, and by that, the dye migration was completelyAbstract A new class of nanocolorants is described for the use as a colorant in hot-melt ink application for ink-jet printing technology. An inverse miniemulsion polymerization process was utilized successfully as a one-step encapsulation process to encapsulate the highly hydrophilic water-soluble fluorescent Rhodamine B dye (RhB) by the hydrophilic water soluble poly(acrylamide) (PAAm). Three types of Rhodamine B-based nanocolorants, PAAm/RhB, crosslinked-PAAm/RhB and poly(AAm-co-Sty)/RhB, were synthesized using inverse miniemulsion polymerization. The PAAm/RhB nanocolorants exhibited solid dark nanoparticles morphology, while crosslinked-PAAm/RhB and poly(AAm-co-Sty)/RhB showed a core-shell type of morphology. The nanocolorants showed improved light and dye migration fastness as well as high thermal stability, especially, nanocolorants with core-shell morphology.supressed. Both poly(AAm-co-RhB) and crosslinked-poly(AAm-co-RhB) nanocolorants showed high thermal stability as well as high Tg values.